What is the yield strength of pure aluminum in PSI?
Table 1: Summary of mechanical properties for 6061 aluminum alloy.
| Mechanical Properties | Metric | English |
|---|---|---|
| Ultimate Tensile Strength | 310 MPa | 45000 psi |
| Tensile Yield Strength | 276 MPa | 40000 psi |
| Shear Strength | 207 MPa | 30000 psi |
| Fatigue Strength | 96.5 MPa | 14000 psi |
What is the yield strength of aluminum?
Aluminum 6061-T6; 6061-T651
| Physical Properties | Metric | English |
|---|---|---|
| Tensile Yield Strength | 276 MPa | 40000 psi |
| Elongation at Break | 12 % | 12 % |
| Elongation at Break | 17 % | 17 % |
| Modulus of Elasticity | 68.9 GPa | 10000 ksi |
What is the tensile strength of aluminum in PSI?
Aluminum – Advantages and Properties of Aluminum
| Property | Minimum Value (S.I.) | Units (Imp.) |
|---|---|---|
| Poisson’s Ratio | 0.32 | NULL |
| Shear Modulus | 25 | 106 psi |
| Tensile Strength | 75 | ksi |
| Young’s Modulus | 68 | 106 psi |
What does the code 1100 tell us about aluminum?
Aluminum 1100: This is commercially pure aluminum, 99% min pure. It is soft, ductile, and has excellent workability which makes it ideal for projects requiring challenging forming operations. It work-hardens slowly, and is not heat-treatable.
How do you increase the yield strength of aluminum?
Common additives used to increase the strength and formability of aluminum include silicon, magnesium and copper. Aluminum-zinc alloys are some of the strongest alloys available today and are commonly used by the automotive and aerospace industries.
Can you heat treat 1100 aluminum?
Aluminium / Aluminum 1100 alloy cannot be successfully heat treated other than to produce the annealed form and ‘O’ temper.
What is 1100 aluminum used for?
Aluminum 1100 is one of the most widely used alloys, with excellent forming properties, especially in the fully soft, annealed temper. It may be suitable for applications that require bending, spinning, drawing, stamping and roll forming.
What do you need to know about 1100 aluminum?
Instead of strength, 1100 is typically used for chemical equipment, food handling equipment, utensils, rivets, decorative trim, decorative parts, dials and name plates, lighting equipment, heat exchangers, and sheet metal work. Also, 1100 aluminum is very sensitive to heat variance.
Which is a better alloy 1100 or 6061?
Typically 1100 aluminum is offered in three alloys. One of the most common questions about 1100 is how it compares to 6061 aluminum. 6061 is the most commonly used aluminum alloy on Earth. It exhibits high strength, low weight, easy machining, good corrosion resistance, and good thermal properties.
What is the tensile strength of an aluminum alloy?
TYPICAL MECHANICAL DATA: Alloy-Temper Tensile Strength (ksi) Yield Strength (ksi) Elongation (%) 1100-O 13 5 30 1100-H14 18 17 3 1100-H18 24 22 2
What kind of applications can 1100 alloy be used for?
1100 is one of the most widely used alloys, with excellent forming properties, especially in the fully soft, annealed temper. It may be suitable for applications that require bending, spinning, drawing, stamping and roll forming. It has good thermal conductivity and is often used in heat exchangers and as a heat sinks in electrical applications.